Baskaran, Dilip Rhaj (2019) Effect Of Ferum Loading On The Properties Of GraphiteCarbon BlackPolypropylene Composite As Bipolar Plate. Project Report. UTeM, Melaka, Malaysia. (Submitted)
![]() |
Text (24 Pages)
Effect Of Ferum Loading On The Properties Of GraphiteCarbon BlackPolypropylene Composite As Bipolar Plate.pdf Download (3MB) |
Abstract
Past few years, they are many processes has been conducting in understanding and improvement of Polymer Electrolyte Membrane Fuel Cell (PEMFC) The performance of PEMFC is relies upon the bipolar plates. This research is about the improvement of bipolar plate through multi-filler application by Ferum were fabricated through a selection of process. They are pre-mixing of raw materials, ball milling, pulverizing and compression molding. For electric conductivity the adding of 10wt% of Ferum plate demonstrates higher conductivity contrasted with other composition. Ferum 10 wt.% plate shows higher flexural strength when compared with others composition. With respect to density and shore hardness, 10wt% Ferum demonstrates unrivaled estimation of 1.489 g/cm³ and 70.8 individually. Therefore, the properties of adding 10 wt.% of Ferum to bipolar plate only composition exceed all target set by US-Department Of Energy.
Item Type: | Final Year Project (Project Report) |
---|---|
Uncontrolled Keywords: | Polymeric composites, Electric conductivity |
Subjects: | T Technology > TA Engineering (General). Civil engineering (General) |
Divisions: | Library > Final Year Project > FKM |
Depositing User: | Sabariah Ismail |
Date Deposited: | 23 Nov 2020 03:05 |
Last Modified: | 23 Nov 2020 03:05 |
URI: | http://digitalcollection.utem.edu.my/id/eprint/24730 |
Actions (login required)
![]() |
View Item |