Saidin, Nur Hidayah (2017) Application Of Palm Oil Fiber-PP Composite For Fabrication On Interior Part Of Automotive Component. Project Report. UTeM, Melaka, Malaysia. (Submitted)
Text (24 Pages)
Application Of Palm Oil Fiber-PP Composite For Fabrication On Interior Part Of Automotive Component.pdf - Submitted Version Download (535kB) |
Abstract
This study investigates the mechanical and physical properties of high impact polypropylene composite reinforced with palm oil fiber. Palm oil fiber was undergo chemical treatment which is alkaline treatment to improve the properties the fiber. Less than 10 mm length of fiber is used with four different fiber loading of PO (10, 20, 30, and 40 wt%) for composite fabrication. The fabrication of composite was conducted by hot press technique. The test that involved in order identify the effect of fiber loading were tensile test, hardness test, density test and scanning electron microscope (SEM). The results of test showed that the PO-PP composite with the 10 wt% fiber loading achieved the highest values of maximum load, tensile stress and tensile strain (extension) which is 1162.21 N, 23.25 MPa, and 0.03624 mm respectively. Meanwhile, for hardness and density, PO-PP composite with 40 wt% fiber loading achieved the highest value which is 64 and 0.997 g/cm3 respectively. The results is influenced by alkaline treatment that change the mechanical properties of the PO-PP composite.
Item Type: | Final Year Project (Project Report) |
---|---|
Uncontrolled Keywords: | Fibrous composites - Mechanical properties, Production engineering, Composite materials, Fibers |
Subjects: | T Technology > T Technology (General) T Technology > TA Engineering (General). Civil engineering (General) |
Divisions: | Library > Final Year Project > FKM |
Depositing User: | Mohd Hannif Jamaludin |
Date Deposited: | 31 Dec 2018 03:23 |
Last Modified: | 31 Dec 2018 03:23 |
URI: | http://digitalcollection.utem.edu.my/id/eprint/22647 |
Actions (login required)
View Item |